PRODUCT INTRODUCTION
Reinforced PP concrete casting panel is a kind of sandwich panel, which is thermoformed by high performance thermoplastic composite and PP hollow core. The continuous fiberglass reinforced thermoplastic composite material is as its surface, PP hollow grid board is as its core.
CIMC Composites’ reinforced PP concrete casting panel has ultra-high mechanical strength and excellent dimensional stability of its surface high-performance thermoplastic composite material. It solves the thermal expansion and contraction of traditional casting panel in the environment of large temperature difference. It reduces the cross-section deviation of concrete, reduces the problem of mold leakage and mold explosion, and improves the quality of concrete construction. At the same time, the new casting panel is light in weight, can be handled manually, reduces equipment investment, avoids the increase of processes, reduces process overlap, greatly improves construction efficiency, and lays a good foundation for later decoration construction, saves decoration costs, and has good economic and social benefits. . This product can exert its performance advantages in some high-demand large-scale projects.
The product uses polypropylene as the main material, which is green and environmentally friendly, tasteless and harmless.
BENEFITES OF PRODUCT
Light weight, only 10kg/m2 ;
Impact resistant and high strength, around 4 times than common plastic concrete casting panel;
Small expansion coefficient, good dimensional stability, the change rate of transverse and longitudinal dimensions after heating is less than 0.2%;
Large plate width, less seams, easy to assemble；
Smooth surface, no need to brush mold release agent, easy mold release；
Waterproof and moisture-proof, mildew resistance, corrosion resistance, cold resistance, high temperature resistance, acid and alkali resistance;
Fire-retardant, flame-resistant, anti-welding slag;
Convenient construction, can be sawed, nailed, welded, and can be processed into any length;
Durable, high turnover rate, can be turned over more than 100 times, and the single-use cost can be reduced to about 1.4 yuan/㎡.
PRODUCT COMPARISON
WOOD PANEL | ALUMINUM PANEL | CIMC PANEL | |
Unit Weight | 13-16kg/m2 | 20-23kg/ m2 | 10kg/ m2 |
Market Price | 50-80 RMB/ m2 | 1000 RMB/ m2 | 140-250 RMB/ m2 |
Turnover | 5-8 times | 100 times | 100 times |
Once cost | 4-16 RMB/ m2 | 10 RMB/ m2 | 1.4-2.5 RMB/ m2 |
Fire retardant | × | √ | √ |
Recycle | × | √ | √ |
Water absorption and deformation | Easy | Not easy | Not easy |
demolding process | Not easy | Not easy | Easy |
Use a release agent | Yes | Yes | No |
Plastering process | Yes | No | No |
Labor cost per m2 | High | Low | Low |
Custom shape | √ | Mandatory | √ |
corrosion resistance | « | ««« | ««««« |
exposure to sunlight | Not good | Good | Good |
concrete surface quality | normal | smooth | smooth |
mold leakage and mold explosion | Yes | No | No |
On-site renovation | Easy | Not easy | Easy |
Applicability | General | Limit | General |
TYPICAL DATA SHEET
Items | Unit | Typical Value | Standard |
Areal density | Kg/m2 | 10 | -- |
water absorption | % | 0.26 | GB/T 1462 |
Shore hardness tester-D | / | 69 | GB/T2411-2008 |
Bending strength | MPa | 61 | JGT418-2013 |
Flexural modulus | MPa | 4935 | JGT418-2013 |
Un-notched Charpy Impact Strength | KJ/㎡ | 60 | GB/T 1451-2005 |
Dimensional change rate after heating | % | Transverse and longitudinal ±0.13 | JGT418-2013 |
Vicat softening temperature | ℃ | 125℃ | GB/T 1633 |
Burning behavior class | / | B2(E) | GB/T 8626-2007 |
Construction minimum temperature | ℃ | -20℃ | / |
The data are laboratory averages, only used as a reference, not product standard
SPECIFICATIONS
Items | Range |
Width | ≤1000mm |
Thickness | 12mm、15mm、18mm |
Length | Can be customized by requirement |
Color | Gray core and natural surface, other color can be customized |
Flammability | Can be customized by requirement， but normally B2(E) level |
CONSTRUCTION SITE PICTURER
 |  |  |  |